Ghazi M, hasanshah M. Synthesis, characterization and investigation of charge ordering transition temperature of La2-xSrxNiO4 (x ≈ 0.33) nanoparticles on particles size. Journal title 2013; 12 (4) :637-656
URL: http://jsci.khu.ac.ir/article-1-1545-en.html
Abstract:   (5354 Views)
Nickelate with general formula La2-xSrxNiO4 (x≈0.33) were synthesized by the sol–gel method. Then by changing the sintering temperature and growth parameters, particles with various sizes were produced. The crystal structure and physical properties of the prepared samples were investigated by X-ray diffraction (XRD), Fourier transform IR spectroscopy (FTIR), Energy dispersive X-ray spectroscopy (EDX) and field emission scanning electron microscopy (FE-SEM) and resistivity measurements from room temperature to low temperatures. The XRD results and investigation of the surface morphology show the lowest temperature to get a single phase tetragonal structure is 920°C. These data confirm the formation of single phase structure in samples sintered at higher temperatures. The particle size increases with increase in sintering temperature. The FE-SEM results show that the particles sizes are in range of 50nm to 2mm. The results of resistivity measurements versus temperature by fourprobe method indicate that the charge ordering transition temperature move to lower temperature with decrease in particle size. 
Full-Text [PDF 1045 kb]   (1325 Downloads)    
Type of Study: S |
Published: 2013/11/15

Add your comments about this article : Your username or Email:

Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2024 CC BY-NC 4.0 | Quarterly Journal of Science Kharazmi University

Designed & Developed by : Yektaweb